BOREALIS Daplen EG103AI
Teknik Özellikler
| Yoğunluk | 1.02 g/cm³ |
|---|---|
| MFR (Eriyik Akış Hızı) | 26.0 g/10min |
| Çekme Dayanımı | 22.0 MPa |
| Charpy (çentikli) | 15.0 kJ/m² |
| HDT (ısıl bükülme) | 105.0 °C |
Açıklama
Daplen EG103AI is a 15% mineral filled polypropylene compound intended for injection moulding. This material has an excellent balance between impact strength and stiffness and high melt flow rate. Applications Daplen EG103AI has been developed especially for the automotive industry. Door panels and pockets Other automotive interior parts Physical Properties Property Typical Value Test Method Data
Uygulamalar
Daplen EG103AI has been developed especially for the automotive industry. Door panels and pockets Other automotive interior parts Physical Properties Property Typical Value Test Method Data should not be used for specification work Density 1020 kg/m³ ISO 1183 Melt Flow Rate (230 °C/2,16 kg) 26 g/10min ISO 1133 Flexural Modulus (2 mm/min) 1.900 MPa ISO 178 Tensile Strength (50 mm/min) 22 MPa ISO 527-2 Heat Deflection Temperature B (0,45 MPa) 105 °C ISO 75-2 Charpy Impact Strength, notched (23 °C) 15 kJ/m² ISO 179/1eA Charpy Impact Strength, notched (-20 °C) 3 kJ/m² ISO 179/1eA Values determined