BOREALIS BJ380MO
Teknik Özellikler
| Yoğunluk | 0.905 g/cm³ |
|---|---|
| MFR (Eriyik Akış Hızı) | 80.0 g/10min |
| Çekme Dayanımı | 25.0 MPa |
| Charpy (çentikli) | 5.0 kJ/m² |
| HDT (ısıl bükülme) | 90.0 °C |
Açıklama
BJ380MO is a very high melt flow heterophasic copolymer with high/medium impact strength and stiffness. This grade is designed for high-speed injection moulding and contains nucleating and antistatic additives. This polymer is a CR (controlled rheology) grade with narrow molecular weight distribution giving low warpage. Components moulded from this grade have good demoulding properties and combine
Uygulamalar
Thin wall containers Closures Square containers Lids Special Features High impact strength Good gloss High stiffness Excellent antistatic properties Physical Properties Property Typical Value Test Method Data should not be used for specification work Density 905 kg/m³ ISO 1183 Melt Flow Rate (230 °C/2,16 kg) 80 g/10min ISO 1133 Flexural Modulus 1.200 MPa ISO 178 Tensile Modulus (1 mm/min) 1.300 MPa ISO 527-2 Tensile Strain at Yield (50 mm/min) 5% ISO 527-2 Tensile Stress at Yield (50 mm/min) 25 MPa ISO 527-2 Heat Deflection Temperature (0,45 N/mm²) 90 °C ISO 75-2 Charpy Impact Strength, notche