BOREALIS Borpact SH950MO
Teknik Özellikler
| Yoğunluk | 0.905 g/cm³ |
|---|---|
| MFR (Eriyik Akış Hızı) | 40.0 g/10min |
| Çekme Dayanımı | 20.0 MPa |
| Eğme Modülü | 950.0 MPa |
| Charpy (çentikli) | 8.0 kJ/m² |
| HDT (ısıl bükülme) | 75.0 °C |
Açıklama
SH950MO is a random heterophasic copolymer intended for injection moulding. This grade yields high transparency and deep freeze impact resistance combined with excellent flow properties. The material is nucleated with Borealis Nucleation Technology (BNT). This grade contains antistatic and demoulding additives which, together with enhanced nucleation, create a high potential for cycle time reducti
Uygulamalar
Ice cream containers Bread boxes, crates Crates Flip top caps, high gloss closures Deep freeze boxes for food storage Special Features Good flow Improved gloss and excellent transparency Good impact strength Very low influence on taste & odour Physical Properties Property Typical Value Test Method Data should not be used for specification work Density 905 kg/m³ ISO 1183 Melt Flow Rate (230 °C/2,16 kg) 40 g/10min ISO 1133 Flexural Modulus 950 MPa ISO 178 Tensile Modulus (50 mm/min) 1.050 MPa ISO 527-2 Tensile Strain at Yield (50 mm/min) 10 % ISO 527-2 Tensile Stress at Yield (50 mm/min) 20 MPa