BOREALIS Bormod BF970MO
Teknik Özellikler
| Yoğunluk | 0.905 g/cm³ |
|---|---|
| MFR (Eriyik Akış Hızı) | 20.0 g/10min |
| Çekme Dayanımı | 27.0 MPa |
| Charpy (çentikli) | 8.0 kJ/m² |
| HDT (ısıl bükülme) | 102.0 °C |
Açıklama
BF970MO is a heterophasic copolymer. This product is characterized by an optimum combination of very high stiffness and high impact strength. This grade uses Borealis Nucleation Technology (BNT) to increase productivity by cycle time reduction. BNT in combination with excellent stiffness and good flow properties creates a high potential for wall-thickness reduction. Products originating from this
Uygulamalar
Crates and boxes Technical parts Pails Special Features High stiffness Good flow behaviour High impact strength Physical Properties Property Typical Value Test Method Data should not be used for specification work Density 905 kg/m³ ISO 1183 Melt Flow Rate (230 °C/2,16 kg) 20 g/10min ISO 1133 Flexural Modulus 1.450 MPa ISO 178 Tensile Modulus (50 mm/min) 1.500 MPa ISO 527-2 Tensile Strain at Yield (50 mm/min) 5% ISO 527-2 Tensile Stress at Yield (50 mm/min) 27 MPa ISO 527-2 Heat Deflection Temperature (0,45 MPa) 1 102 °C ISO 75-2 Charpy Impact Strength, notched (23 °C) 8 kJ/m² ISO 179/1eA Charp