BOREALIS Bormod BE961MO
Teknik Özellikler
| Yoğunluk | 0.905 g/cm³ |
|---|---|
| MFR (Eriyik Akış Hızı) | 12.0 g/10min |
| Çekme Dayanımı | 23.0 MPa |
| Charpy (çentikli) | 13.0 kJ/m² |
| HDT (ısıl bükülme) | 92.0 °C |
Açıklama
BE961MO is a heterophasic copolymer. This grade is characterized by an optimum combination of high stiffness, low creep and very high impact strength. This grade uses Borealis Nucleation Technology (BNT) to increase productivity by cycle time reduction. BNT in combination with excellent stiffness and good flow properties creates a high potential for wall-thickness reduction. Products originating f
Uygulamalar
Crates and boxes Luggage Pails Technical parts Special Features High stiffness Low creep performance High impact strength Good flow behaviour Physical Properties Property Typical Value Test Method Data should not be used for specification work Density 905 kg/m³ ISO 1183 Melt Flow Rate (230 °C/2,16 kg) 12 g/10min ISO 1133 Flexural Modulus 1.250 MPa ISO 178 Tensile Modulus (50 mm/min) 1.200 MPa ISO 527-2 Tensile Strain at Yield (50 mm/min) 5,3 % ISO 527-2 Tensile Stress at Yield (50 mm/min) 23 MPa ISO 527-2 Heat Deflection Temperature (45 N/mm²) 1 92 °C ISO 75-2 Charpy Impact Strength, notched (