BOREALIS Borealis PP BJ368MO
Teknik Özellikler
| Yoğunluk | 0.905 g/cm³ |
|---|---|
| MFR (Eriyik Akış Hızı) | 70.0 g/10min |
| Çekme Dayanımı | 25.0 MPa |
| Charpy (çentikli) | 5.5 kJ/m² |
| HDT (ısıl bükülme) | 102.0 °C |
Açıklama
BJ368MO is a polypropylene copolymer characterized by good flow, and optimum combination of high stiffness and high impact strength. The material is nucleated with Borealis Nucleation Technology (BNT). Flow properties, nucleation and good stiffness give potential for cycle time reduction. The material have good antistatic performance and good mould release properties. CAS-No. 9010-79-1 Application
Uygulamalar
Thin wall containers Special Features stiffness and impact balance Reduced cycle time and increased output Good flow behaviour Physical Properties Property Typical Value Test Method Data should not be used for specification work Density 905 kg/m³ ISO 1183 Melt Flow Rate (230 °C/2,16 kg) 70 g/10min ISO 1133 Flexural Modulus 1.500 MPa ISO 178 Tensile Modulus (50 mm/min) 1.500 MPa ISO 527-2 Tensile Strain at Yield (50 mm/min) 4% ISO 527-2 Tensile Stress at Yield (50 mm/min) 25 MPa ISO 527-2 Heat Deflection Temperature 102 °C ISO 75-2 Charpy Impact Strength, notched (23 °C) 5,5 kJ/m² ISO 179/1eA C