BOREALIS Borcoat EA165E
Teknik Özellikler
| Yoğunluk | 0.9 g/cm³ |
|---|---|
| MFR (Eriyik Akış Hızı) | 0.3 g/10min |
| Erime Noktası | 164.0 °C |
| Çekme Dayanımı | 22.0 MPa |
| Çekme Modülü | 900.0 MPa |
| Charpy (çentikli) | 70.0 kJ/m² |
| Vicat | 133.0 °C |
| Sertlik | 60.0 - |
Açıklama
Borcoat EA165E is an elastomer modified compound, based on a high molecular weight copolymer. The elastomer modification gives excellent low temperature impact resistance. The product can be self coloured. Applications Borcoat EA165E is used for injection moulded field joints, moulded articles and impact resistant external coatings. Physical Properties Property Typical Value Test Method Data shoul
Uygulamalar
Borcoat EA165E is used for injection moulded field joints, moulded articles and impact resistant external coatings. Physical Properties Property Typical Value Test Method Data should not be used for specification work Density (Compound) 1 900 kg/m³ ISO 1183-1, Method A Melt Flow Rate (230 °C/2,16 kg) 0,3 g/10min ISO 1133 Tensile Modulus (2 mm/min) 900 MPa ISO 527-2 Tensile Strain at Yield (50 mm/min) (23 °C) 16 % ISO 527-2 Tensile Strain at Break (50 mm/min) (23 °C) 400 % ISO 527-2 Tensile Stress at Yield (50 mm/min) (23 °C) 22 MPa ISO 527-2 Melting temperature 164 °C ISO 11357-3 Oxidation Ind