UZ-KOR HDPE BL6200
Teknik Özellikler
| Yoğunluk | 0.956 g/cm³ |
|---|---|
| MFR (Eriyik Akış Hızı) | 0.32 g/10min |
| Çekme Dayanımı | 240.0 MPa |
| Eğme Modülü | 11000.0 MPa |
| Vicat | 123.0 °C |
| Sertlik | 52.0 - |
| Kopma Uzaması | 500.0 % |
Açıklama
BL6200- is a HDPE resin produced via Slurry process technology and suitable for use in blow moulding application. BL6200 is designed to offer high speed processability, good ESCR. Application Bottle (small) and household product (shampoo, bleach, Cosmetics). Properties Physical Testing methods Nominal values Density ASTM D 1505 g/cm3 0,956-0,961 Melt Flow Rate ASTM D 1238 g/10min 0,32-0,47 Mechani
Uygulamalar
Bottle (small) and household product (shampoo, bleach, Cosmetics). Properties Physical Testing methods Nominal values Density ASTM D 1505 g/cm3 0,956-0,961 Melt Flow Rate ASTM D 1238 g/10min 0,32-0,47 Mechanical Tensile Strength at Yield (min.) ASTM D 638 kg/сm2 240 2 Tensile Strength at Break (min.) ASTM D 638 kg/сm NB Elongation at Break (min.) ASTM D 638 % 500 2 Flexural Modulus (min.) ASTM D 790 kg/сm 11000 Impact Izod Impact Strength (23⁰C) (min.) ASTM D 256 kg cm/cm 11 Thermal 0 Vicat Softening Point (min.) ASTM D 1525 C 123 Additional properties Rockwell Hardness (min.) ASTM D785 R 52 E