REPSOL PRIMEVA P2430C
Teknik Özellikler
| Yoğunluk | 0.944 g/cm³ |
|---|---|
| MFR (Eriyik Akış Hızı) | 3.0 g/10min |
| Çekme Dayanımı | 25.0 MPa |
| Sertlik | 79.0 - |
| Kopma Uzaması | 740.0 % |
Açıklama
Melt flow rate (190ºC, 2.16kg) 3.0 g/10 min ISO 1133 Vinyl acetate content 24 % Internal Density at 23 °C 944 kg/m3 ISO 1183 Ring-ball softening point 162 ºC ASTM E-28 Melting point 77 ºC Internal Viscosity Brookfield 180ºC (Spindle SC4-27) 3728000 cP Internal Viscosity Brookfield 200ºC (Spindle SC4-27) 6696000 cP Internal Mechanical Tensile strength at break 25 MPa ISO 527-2 Elongation at break 7
Uygulamalar
Injection moulding. Release agents containing silicone must be avoided. Blends with waxes. Manufacture of masterbatches. Microcellular foams. Extrusion of profiles and sheets with high flexibility. Can be used to produce halogen-free-flame-retardant (HFFR) cables compounds. Recommended melt temperature below 200ºC to avoid the decomposition of the polymer. Processing conditions should be optimised for each production line.