LYONDELLBASELL Hostacom SP98F_94
Teknik Özellikler
| Yoğunluk | 1.13 g/cm³ |
|---|---|
| MFR (Eriyik Akış Hızı) | 6.0 g/10min |
| Çekme Dayanımı | 21.0 MPa |
| Eğme Modülü | 94.0 MPa |
| HDT (ısıl bükülme) | 110.0 °C |
Açıklama
Hostacom SP98/F/94 Black conventional melt flow, 2,200 MPa flexural modulus, mineral-filled thermoplastic elastomeric olefin (TEO) resin has a very good combination of stiffness, impact resistance and surface appearance. It was designed primarily for large part injection molded automotive interior and exterior applications. Product Characteristics Status Commercial: Active Test Method used ISO Ava
Uygulamalar
Typical Properties Method Value Unit Physical Density ISO 1183 1.13 g/cm³ Melt flow rate (MFR) (230°C/2.16Kg) ISO 1133 6 g/10 min Note: Alternative test method is ASTM D 1238-01. Mechanical Tensile Stress at Yield ISO 527-1, -2 21 MPa Tensile Strain at Break ISO 527-1, -2 25 MPa Flexural modulus ISO 178 2200 MPa Impact Notched izod impact strength (23 °C) ISO 180 7.5 kJ/m² Thermal Heat deflection temperature B (0.45 MPa) ISO 75B-1, -2 110 °C Unannealed Notes Typical properties; not to be construed as specifications. © LyondellBasell Industries Holdings, B.V. 2012 LyondellBasell markets this pr