LYONDELLBASELL Hostacom M2 U02
Teknik Özellikler
| Yoğunluk | 1.04 g/cm³ |
|---|---|
| MFR (Eriyik Akış Hızı) | 11.0 g/10min |
| MVR | 10.0 cm³/10min |
| Çekme Dayanımı | 34.0 MPa |
| Çekme Modülü | 2600.0 MPa |
| Eğme Modülü | 2900.0 MPa |
| Charpy (çentikli) | 45.0 kJ/m² |
| HDT (ısıl bükülme) | 120.0 °C |
| Sertlik | 95.0 - |
Açıklama
"Hostacom" M2 U02 is a 20% mineral filled PP homopolymer with high stiffness, low warpage. Used for air conditioning units. It is not intended for medical, pharmaceutical or drinking water applications. Product Characteristics Status Commercial: Active Test Method used ISO Availability Europe Features Homopolymer, Good Stiffness , Low Warpage Typical Customer Applications Automotive Parts, Under-t
Uygulamalar
Typical Properties Method Value Unit Physical Density ISO 1183 1.04 g/cm³ Melt flow rate (MFR) (230°C/2.16Kg) ISO 1133 11 g/10 min Melt volume flow rate (230°C/2.16Kg) ISO 1133 12.5 cm³/10min Mechanical Tensile Modulus (Secant) ISO 527-1, -2 2600 MPa Tensile Stress at Yield (50 mm/min) ISO 527-1, -2 34 MPa Tensile Strain at Yield (50 mm/min) ISO 527-1, -2 6.0 % Flexural modulus (Secant) ISO 178 2900 MPa Flexural Stress (3.5 %) ISO 178 47 MPa Impact Charpy unnotched impact strength (23 °C, Type 1, ISO 179 45 kJ/m² Edgewise) Charpy notched impact strength (23 °C, Type 1, ISO 179 4.0 kJ/m² Edgewi