LYONDELLBASELL Hostacom HRC 114T BLACK
Teknik Özellikler
| Yoğunluk | 1.2 g/cm³ |
|---|---|
| MFR (Eriyik Akış Hızı) | 23.0 g/10min |
| MVR | 10.0 cm³/10min |
| Çekme Dayanımı | 28.0 MPa |
| Çekme Modülü | 4000.0 MPa |
| Eğme Modülü | 4000.0 MPa |
| Charpy (çentikli) | 20.0 kJ/m² |
| HDT (ısıl bükülme) | 72.0 °C |
Açıklama
"Hostacom" HRC 114T is a 40% mineral filled elastomer modified polypropylene homopolymer for injection molding. It has a high flowability. The grade has been specifically designed for molding Automotive Under the Hood and Interior parts. The grade is available black colour, pellet form. Product Characteristics Status Commercial: Active Test Method used ISO Availability Europe Features High Flow Ty
Uygulamalar
Typical Properties Method Value Unit Physical Density (Method A) ISO 1183 1.20 g/cm³ Melt flow rate (MFR) (230°C/2.16Kg) ISO 1133 23 g/10 min Melt volume flow rate (230°C/2.16Kg) ISO 1133 22.0 cm³/10min Mechanical Tensile Modulus (Secant) ISO 527-1, -2 4000 MPa Tensile Stress at Yield (50 mm/min) ISO 527-1, -2 28.0 MPa Tensile Strain at Yield (50 mm/min) ISO 527-1, -2 4.0 % Flexural modulus (Secant) ISO 178 4000 MPa Impact Charpy unnotched impact strength (23 °C, Type 1, ISO 179 20.0 kJ/m² Edgewise) Charpy notched impact strength (23 °C, Type 1, ISO 179 3.00 kJ/m² Edgewise, Notch A) Thermal He