LYONDELLBASELL Hifax CA 138 A
Teknik Özellikler
| Yoğunluk | 0.88 g/cm³ |
|---|---|
| MFR (Eriyik Akış Hızı) | 2.8 g/10min |
| Erime Noktası | 163.0 °C |
| Çekme Dayanımı | 10.0 MPa |
| Eğme Modülü | 500.0 MPa |
| HDT (ısıl bükülme) | 58.0 °C |
| Vicat | 90.0 °C |
| Sertlik | 41.0 - |
Açıklama
Hifax CA 138 A is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell's proprietary Catalloy process technology. This grade is suitable for use in compounds as impact modifier, to give excellent processability whilst maintaining optimum mechanical properties. The grade is available in natural pellet form. Regulatory Status For regulatory compliance information, see Hifax
Uygulamalar
Market Automotive; Compounding; Consumer Products Processing Method Compounding; Extrusion Flat-die; Injection Molding; Sheet Attribute Good Moldability; Good Processability; High Impact Resistance; Low Temperature Impact Resistance Nominal Typical Properties Value Units Test Method Physical Melt Flow Rate, (230 °C/2.16 kg) 2.8 g/10 min ISO 1133-1 Density, (23 °C, Method A) 0.88 g/cm³ ISO 1183-1 Mechanical Flexural Modulus 500 MPa ISO 178 Tensile Stress at Break 10 MPa ISO 527-1, -2 Tensile Stress at Yield 17 MPa ISO 527-1, -2 Tensile Strain at Break 400 % ISO 527-1, -2 Tensile Strain at Yield