LOTTE Lotte TC-8001G
Teknik Özellikler
| MFR (Eriyik Akış Hızı) | 9.0 g/10min |
|---|---|
| Çekme Dayanımı | 50.0 MPa |
| Eğme Modülü | 54.0 MPa |
| Izod (çentikli) | 6.0 J/m |
| Vicat | 50.0 °C |
Açıklama
Thermal conductive, 20% graphite filled Medium viscosity, easy mold release Available in opaque color only Applications Heat sinks, cooling units, electric/electronic housings, etc. Typical properties1 Test Method Typical value Unit Physical Melt Flow Index, 300℃, 1.2 kg ASTM D1238 9 g/10min Specific Gravity ASTM D792 1.28 Mold Shrinkage HPC method 0.4 ~ 0.6 % Mechanical Tensile Strength, yield, 5
Uygulamalar
Heat sinks, cooling units, electric/electronic housings, etc. Typical properties1 Test Method Typical value Unit Physical Melt Flow Index, 300℃, 1.2 kg ASTM D1238 9 g/10min Specific Gravity ASTM D792 1.28 Mold Shrinkage HPC method 0.4 ~ 0.6 % Mechanical Tensile Strength, yield, 50 mm/min ASTM D638 470 kgf/cm2 Tensile Elongation, break, 50 mm/min ASTM D638 - % Flexural Strength, yield, 10 mm/min ASTM D790 670 kgf/cm2 Flexural Modulus, 10 mm/min ASTM D790 54,000 kgf/cm2