LOTTE Lotte PCG-2300
Teknik Özellikler
| MFR (Eriyik Akış Hızı) | 1.2 g/10min |
|---|---|
| Çekme Dayanımı | 1.3 MPa |
| Eğme Modülü | 75.0 MPa |
| Izod (çentikli) | 12.0 J/m |
| Vicat | 50.0 °C |
Açıklama
30% glass-fiber reinforced, easy mold release Optimum combination of high modulus and impact strength Applications Multi purpose grade (electric/electronic housings, etc.) Typical properties1 Test method Typical value Unit Physical Melt Flow Index, 300°C, 1.2 kg ASTM D1238 - g/10 min Specific Gravity ASTM D792 1.42 Mold Shrinkage ASTM D955 0.1~0.3 % Mechanical Tensile Strength, yield, 50 mm/min AS
Uygulamalar
Multi purpose grade (electric/electronic housings, etc.) Typical properties1 Test method Typical value Unit Physical Melt Flow Index, 300°C, 1.2 kg ASTM D1238 - g/10 min Specific Gravity ASTM D792 1.42 Mold Shrinkage ASTM D955 0.1~0.3 % Mechanical Tensile Strength, yield, 50 mm/min ASTM D638 1,300 kgf/cm2 Tensile Elongation, break, 50 mm/min ASTM D638 - % Flexural Strength, yield, 10 mm/min ASTM D790 1,900 kgf/cm2 Flexural Modulus, 10 mm/min ASTM D790 75,000 kgf/cm2