LOTTE Lotte PC-1600
Teknik Özellikler
| MFR (Eriyik Akış Hızı) | 62.0 g/10min |
|---|---|
| Çekme Dayanımı | 50.0 MPa |
| Izod (çentikli) | 8.0 J/m |
| Vicat | 50.0 °C |
Açıklama
Ultra low viscosity, No colorant Applications Compound raw material Typical properties1 Test Method Typical value Unit Physical Melt Flow Index, 300℃, 1.2kg ASTM D1238 62 g/10min Specific Gravity ASTM D792 1.20 Mold Shrinkage ASTM D955 0.5~0.7 % Mechanical Tensile Strength, yield, 50mm/min ASTM D638 630 kgf/cm2 Tensile Elongation, break, 50mm/min ASTM D638 50 % Flexural Strength, yield, 10mm/min A
Uygulamalar
Compound raw material Typical properties1 Test Method Typical value Unit Physical Melt Flow Index, 300℃, 1.2kg ASTM D1238 62 g/10min Specific Gravity ASTM D792 1.20 Mold Shrinkage ASTM D955 0.5~0.7 % Mechanical Tensile Strength, yield, 50mm/min ASTM D638 630 kgf/cm2 Tensile Elongation, break, 50mm/min ASTM D638 50 % Flexural Strength, yield, 10mm/min ASTM D790 920 kgf/cm2 Flexural Modulus, 10mm/min ASTM D790 24,000 kgf/cm2