LOTTE Lotte LX-7000
Teknik Özellikler
| MFR (Eriyik Akış Hızı) | 8.5 g/10min |
|---|---|
| Çekme Dayanımı | 50.0 MPa |
| Izod (çentikli) | 80.0 J/m |
| Vicat | 150.0 °C |
Açıklama
High viscosity, high impact strength Easy mold release Applications Light diffusion grade Typical properties1 Test method Typical value Unit Physical Melt Flow Index, 300°C, 1.2 kg ASTM D1238 8.5 g/10 min Specific Gravity ASTM D792 1.2 Mold Shrinkage ASTM D955 0.5~0.7 % Mechanical Tensile Strength, yield, 50 mm/min ASTM D638 620 kgf/cm2 Tensile Elongation, break, 50 mm/min ASTM D638 > 100 % Flexur
Uygulamalar
Light diffusion grade Typical properties1 Test method Typical value Unit Physical Melt Flow Index, 300°C, 1.2 kg ASTM D1238 8.5 g/10 min Specific Gravity ASTM D792 1.2 Mold Shrinkage ASTM D955 0.5~0.7 % Mechanical Tensile Strength, yield, 50 mm/min ASTM D638 620 kgf/cm2 Tensile Elongation, break, 50 mm/min ASTM D638 > 100 % Flexural Strength, yield, 10 mm/min ASTM D790 900 kgf/cm2 Flexural Modulus, 10 mm/min ASTM D790 24,000 kgf/cm2