LOTTE JH-370A
Teknik Özellikler
| Yoğunluk | 0.9 g/cm³ |
|---|---|
| MFR (Eriyik Akış Hızı) | 27.0 g/10min |
| Çekme Dayanımı | 23.0 MPa |
| HDT (ısıl bükülme) | 105.0 °C |
Açıklama
JH-370A is high impact block copolymer with high ethylene content as co-monomer. This grade is designed to be processed in conventional Injection molding equipment and base resin for compounding. JH-370A shows extremely high impact resistance at low temperature and has also high strength. Applications General articles, Home appliances Automotive compound base resin Physical Properties1 Physical Te
Uygulamalar
General articles, Home appliances Automotive compound base resin Physical Properties1 Physical Test Method Nominal Values Melt Flow Index ASTM D1238 27 g/10min Density ASTM D792 0.9 g/cm3 Mechanical Tensile Stress (Yield) ASTM D638 230 kgf/cm2 23 MPa Tensile Strain (Break) ASTM D638 >100 % >100 % Flexural Modulus ASTM D790 12,500 kgf/cm2 1,230 MPa Impact Notched Izod Impact Strength (23℃) ASTM D256 10.0 kgf·cm/cm 98 J/m Notched Izod Impact Strength (-10℃) ASTM D256 5.0 kgf·cm/cm 49 J/m Thermal Heat Deflection Temperature (4.6kgf/cm2) ASTM D648 105 ℃ Additional Properties Flammability UL94 HB