LOTTE JH-350
Teknik Özellikler
| Yoğunluk | 0.9 g/cm³ |
|---|---|
| MFR (Eriyik Akış Hızı) | 10.0 g/10min |
| Çekme Dayanımı | 23.0 MPa |
| Eğme Modülü | 880.0 MPa |
| HDT (ısıl bükülme) | 100.0 °C |
Açıklama
JH-350 is high impact block copolymer with high ethylene content as co-monomer. This grade is designed to be processed in conventional Injection molding equipment and base resin for compounding. JH-350 shows extremely high impact resistance at low temperature and has also high strength. Applications General articles Automotive compound base resin Physical Properties1 Physical Test Method Nominal V
Uygulamalar
General articles Automotive compound base resin Physical Properties1 Physical Test Method Nominal Values Melt Flow Index ASTM D1238 10 g/10min Density ASTM D792 0.9 g/cm3 Mechanical Tensile Stress (Yield) ASTM D638 230 kgf/cm2 23 MPa Tensile Strain (Break) ASTM D638 >100 % >100 % Flexural Modulus ASTM D790 11,000 kgf/cm2 1,080 MPa Impact Notched Izod Impact Strength (23℃) ASTM D256 12.0 kgf·cm/cm 118 J/m Notched Izod Impact Strength (-10℃) ASTM D256 5.5 kgf·cm/cm 54 J/m Thermal Heat Deflection Temperature (4.6kgf/cm2) ASTM D648 100 ℃ Additional Properties Flammability UL94 HB