LG CHEM LG Chem 314HF-NP (HIPS)
Teknik Özellikler
| MFR (Eriyik Akış Hızı) | 11.0 g/10min |
|---|---|
| Çekme Dayanımı | 190.0 MPa |
| Eğme Modülü | 2000.0 MPa |
| Izod (çentikli) | 8.5 J/m |
| HDT (ısıl bükülme) | 80.0 °C |
| Vicat | 94.0 °C |
| Sertlik | 93.0 - |
Açıklama
Application: High Impact Strength & High Flow grade TV cabinets, High flow length moulds etc Properties Test Method Test Condition Unit Typical Value Physical Specific Gravity ASTM D 792 - - 1.03 Shrinkage ASTM D 955 - % 0.4-0.8 Rheological Melt Flow Index ASTM D 1238 (G) 200 °C / 5 kg gms / 10min 11 Thermal & Optical Vicat Softening point ASTM D 1525 120 °C / Hr, 1 kg °C 94 Heat Deflection temper
Uygulamalar
High Impact Strength & High Flow grade TV cabinets, High flow length moulds etc Properties Test Method Test Condition Unit Typical Value Physical Specific Gravity ASTM D 792 - - 1.03 Shrinkage ASTM D 955 - % 0.4-0.8 Rheological Melt Flow Index ASTM D 1238 (G) 200 °C / 5 kg gms / 10min 11 Thermal & Optical Vicat Softening point ASTM D 1525 120 °C / Hr, 1 kg °C 94 Heat Deflection temperature ASTM D 648 1.82 Mpa °C 80 Flammability UL 94 3.2 mm Rating HB Mechanical Tensile Strength @ Yield, 3.2 mm ASTM D 638 50 mm / min Kg / cm2 190 Tensile Elongation @ Break, 3.2 mm ASTM D 638 50 mm / min % 50 2