LG CHEM LG Chem 312HGH-NP (HIPS)
Teknik Özellikler
| MFR (Eriyik Akış Hızı) | 5.5 g/10min |
|---|---|
| Çekme Dayanımı | 300.0 MPa |
| Eğme Modülü | 5000.0 MPa |
| Izod (çentikli) | 9.5 J/m |
| HDT (ısıl bükülme) | 82.0 °C |
| Vicat | 97.0 °C |
| Sertlik | 103.0 - |
Açıklama
Application: High Gloss HIPS with very High Impact Strength AC grills, Washing Machine top, Cap layer etc., Properties Test Method Test Condition Unit Typical Value Physical Specific Gravity ASTM D 792 - - 1.03 Shrinkage ASTM D 955 - % 0.4-0.8 Rheological Melt Flow Index ASTM D 1238 (G) 200 °C / 5 kg gms / 10min 5.5 Thermal & Optical Vicat Softening point ASTM D 1525 120 °C / Hr, 1 kg °C 97 Heat D
Uygulamalar
High Gloss HIPS with very High Impact Strength AC grills, Washing Machine top, Cap layer etc., Properties Test Method Test Condition Unit Typical Value Physical Specific Gravity ASTM D 792 - - 1.03 Shrinkage ASTM D 955 - % 0.4-0.8 Rheological Melt Flow Index ASTM D 1238 (G) 200 °C / 5 kg gms / 10min 5.5 Thermal & Optical Vicat Softening point ASTM D 1525 120 °C / Hr, 1 kg °C 97 Heat Deflection temperature ASTM D 648 1.82 Mpa °C 82 Flammability UL 94 3.2 mm Rating HB 0 Gloss at 60 angle ASTM D 2457 - - 100 Mechanical Tensile Strength @ Yield, 3.2 mm ASTM D 638 50 mm / min Kg / cm2 300 Tensile E