DAELIM Daelim Po1y LH4100BL
Teknik Özellikler
| Yoğunluk | 0.959 g/cm³ |
|---|---|
| MFR (Eriyik Akış Hızı) | 0.31 g/10min |
| Erime Noktası | 130.0 °C |
| Çekme Dayanımı | 400.0 MPa |
| Vicat | 126.0 °C |
| Kopma Uzaması | 600.0 % |
Açıklama
PE 100 Equivalent Materials Hexene Comonomer Characteristics Outstanding Stress Cracking Excellent Impact Resistance & Resistance Durability Water & Gas Pipe Applications Oil & Engineering Pipe Processing Processing Temperature 190~ 220℃ Recommendation Specification data Complies with FDA 21 CFR 177. 1520 Physical Properties Resin Properties Unit Test Method LH4100BL Density g/㎤ ASTM D
Uygulamalar
Oil & Engineering Pipe Processing Processing Temperature 190~ 220℃ Recommendation Specification data Complies with FDA 21 CFR 177. 1520 Physical Properties Resin Properties Unit Test Method LH4100BL Density g/㎤ ASTM D1505 0.959 Melt Index (190℃, 5.0kg) g/10min ASTM D1238 0.31 Vicat Softening Point ℃ ASTM D1525 126 Melting Temperature ℃ ASTM D3418 130 Additives - - AO, PPA Sheet Properties Unit Test Method LH4100BL Tensile Strength at Break kg/㎠ ASTM D638 400 Elongation at Break % ASTM D638 >600 Flexural Modulus kg/㎠ ASTM D790 Non Break Izod Impact Strength (Notch, -30℃) ㎏-㎝/㎝ ASTM D256 8,000