BRASKEM Braskem PE HDB0358_1
Teknik Özellikler
| MFR (Eriyik Akış Hızı) | 0.3 g/10min |
|---|---|
| Çekme Dayanımı | 30.0 MPa |
| Çekme Modülü | 1420.0 MPa |
| Eğme Modülü | 1500.0 MPa |
| Kopma Uzaması | 500.0 % |
Açıklama
HDB0358 is a bimodal high-density polyethylene copolymer grade. It has an outstanding stiffness and environmental stress crack resistance (ESCR) balance making it ideal for use in a wide range of blow moulding applications. This grade is particularly well suited to chemical and detergent packaging as the exceptional ESCR can allow for significant bottle weight reduction. Application: Blow molded c
Uygulamalar
Blow molded containers up to 25 liters capacity for packaging chemicals, many household products, oils and foodstuffs. Sheet and Corrugated Pipe Extrusion. Process: Blow Molding and Extrusion. Control Properties: Test Methods Units Values Melt Flow Rate (190°C/2.16Kg) ASTM D1238 g/10min 0.300 Density ASTM D792 g/cm3 0.958 Typical Properties1: Test Methods Units Values Tensile Strength at Yield ASTM D638 MPa 30 Elongation at break ASTM D638 % >500 Tensile Modulus of Elasticity, Secant 1% Method ASTM D638 MPa 1420 Flexural Modulus, Secant 1% Method ASTM D790 MPa 1500 Izod Impact Strength ASTM D2